The effect of vanadium on modified Z-phase characteristics in austenitic steels

Citation: Vodárek, V.; Holešinský, J.; Kuboˇn, Z.; Palupˇcíková, R.; Hradeˇcný, K.; Váˇnová, P.; Hlinka, J. The Effect of Vanadium on Modified Z-Phase Characteristics in Austenitic Steels. Crystals 2023,13, 676. https://doi.org/10.3390/ cryst13040676 Academic Editors: Mousa Javidani, Mohammad Jahazi, Akbar Heidarzadeh, Amir Hadadzadeh, Max Hoßfeld and Bolv Xiao Received: 3 March 2023 Revised: 24 March 2023 Accepted: 11 April 2023 Published: 14 April 2023 Copyright: © 2023 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https:// creativecommons.org/licenses/by/ 4.0/). crystals Article The Effect of Vanadium on Modified Z-Phase Characteristics in Austenitic Steels Vlastimil Vodárek 1,*, Jan Holešinský2, Zdenˇek Kuboˇn 3, Renáta Palupˇcíková1, Kryštof Hradeˇcný1, Petra Váˇnová1and Josef Hlinka 1 1Department of Materials Engineering and Recycling, Faculty of Materials Science and Technology, VSB-Technical University of Ostrava, Poruba, 708 30 Ostrava, Czech Republic 2ˇ CEZ, a.s., Duhová2/1444, 140 53 Prague, Czech Republic 3MATERIAL AND METALLURGICAL RESEARCH, Ltd., Pohraniˇcní31, Vítkovice, 706 02 Ostrava, Czech Republic *Correspondence: vlastimil.vodar[email protected] Abstract: In austenitic steels, the tetragonal Z-phase (NbCrN) has frequently been credited with beneficial strengthening effects during dislocation creep. In the modified Z-phase, niobium is partially substituted by vanadium. The basic objective of this contribution is a detailed characterization of the modified Z-phase in vanadium bearing austenitic AISI 316LN+Nb+V and HR3C steels. Experimental activities were focused on crystallography, thermodynamic and dimensional stability, kinetics of precipitation (TTP diagram) and solvus temperature of the modified Z-phase in the steels examined. Thermodynamic modelling was used for prediction of stable minor phases and solvus temperature of the modified Z-phase. Kinetics of precipitation of the (Nb,V)CrN phase in the AISI 316LN+Nb+V steel was experimentally investigated in the temperature interval of 550–1250 ◦ C. The kinetics of precipitation of the modified Z-phase in austenitic matrix was fast. Results of diffraction studies on particles of the modified Z-phase confirmed the existence of the tetragonal unit cell already after short-term annealing. The solvus temperature of the modified Z-phase in austenitic steels was determined to be lower than that for the NbCrN phase. The decrease in the solvus temperature is dependent on the vanadium content in austenitic steels. Both thermodynamic calculations and experimental results proved that the thermodynamical stability of the modified Z-phase in austenite was high. More data are needed for evaluation of long-term dimensional stability of the (Nb,V)CrN phase in austenitic steels at temperatures for their engineering applications. Keywords: AISI 316LN+Nb+V; Super 304H; modified Z-phase; crystal structure; solvus temperature; thermodynamic stability; dimensional stability 1. Introduction In last decades, service conditions of components for advanced power plants have increased, imposing more severe requirements on creep properties and corrosion resistance of high temperature materials [ 1 – 3 ]. Much effort has been devoted to the development of new heat resistant steels, both martensitic and austenitic, and to better understand their microstructure–property relationships. Small changes in the chemical composition of heat resistant steels can lead to substantial changes in their creep resistance [ 1 ]. Creep properties of heat resistant steels in the field of dislocation creep are controlled by the evolution of dislocation substructure, and the formation and growth of sub-grains [ 4 ]. Evolution of dislocation structure is strongly affected by the formation, coarsening and dissolution of minor phases [ 3 ]. Generally, the matrix solid solution and the precipitation hardening associated with a high density of fine, both thermodynamically and dimensionally stable, precipitates provide resistance to dislocation creep. Increasing the extent of precipitation strengthening is one of the most successful methods for improving creep resistance of high Crystals 2023,13, 676. https://doi.org/10.3390/cryst13040676 https://www.mdpi.com/journal/crystals Crystals 2023,13, 676 2 of 16 temperature materials [ 1 ]. Although many minor phases are now well documented, there are still contradictions and missing thermodynamic data about some minor phases [5,6]. Advanced austenitic heat resistant steels are often alloyed by niobium and nitrogen, which allow it to precipitate a complex nitride called Z-phase (NbCrN) [ 7 – 18 ]. Fine particles of this minor phase in austenitic heat resistant steels have frequently been credited with beneficial strengthening during creep [ 7 , 11 ]. Conditions for the Z-phase formation are not clear. Robinson and Jack [ 19 ] reported the formation of Z-phase from solid solution, while Knowles [ 20 ] described its formation from MX precipitates. The results must be examined carefully as the steel compositions were different. The solvus temperature of the NbCrN phase in austenitic stainless steels was reported to be between 1250 and 1350 ◦ C, depending on the steel composition [ 6 ]. Z-phase particles in the AISI 316LN+Nb steel nucleated from solid solution and formed short rods elongated in the [001] Z direction. This is in accordance with the minimum directional mismatch, but some particles exhibited roughly comparable growth in the [001] Z direction and in the <100> Z directions lying in the base plane [ 21 ]. In advanced austenitic steels, Z-phase often nucleates on MX (NbN) particles and forms thin plates [22,23]. The structure of Z-phase was studied by Ettmayer [ 24 ] and by Jack and Jack [ 25 ]. Ettmayer [ 24 ] studied the synthesized complex nitrides NbCrN and reported a tetragonal unit cell with parameters a = 0.4283 nm and c = 0.7361 nm, space group F4bm. Jack and Jack [ 25 ] studied Z-phase in an austenitic steel and interpreted all the X-ray data by a tetragonal cell of dimensions a = 0.3037 nm, c = 0.7391 nm. The relationship between this unit cell and that of the Ettmayer’s cell in the basal plane is √2aJACK =aETTM. . For the unit cell proposed by Jack and Jack [ 25 ] systematic absences occur for hk0 when h + k = 2n + 1. Trial and error methods showed that Z-phase is a complex nitride with ideal composition Nb 2 Cr 2 N 2 . The metal atom arrangement is characterised by double layers of similar atoms alternating along the c axis to provide an AABBAABBAA sequence. In martensitic (9–12) %Cr steels, niobium in the Z-phase has been found to be partially substituted by vanadium and this results in a reduction of the tetragonal unit cell of this modified Z-phase ((Nb,V)CrN): a = 0.286 nm and c = 0.739 nm) [ 26 ]. In the temperature range of 600–650 ◦ C, the Z-phase is the most stable nitride in (9–12) %Cr steels. The formation of the modified Z-phase is slow and is associated with the decomposition of fine nitrides of MX ((Nb,V)N), which significantly contributes to precipitation hardening [26–28] . The modified Z-phase forms large particles and is generally regarded as a harmful minor phase in these steel grades [3]. Extensive studies revealed that the FCC precursor with a lattice parameter a = 0.405 nm can coexist with the tetragonal unit cell of the Z-phase [ 29 , 30 ]. It was reported that during ageing of 12CrMoVNbN steels at 600 ◦ C, the cubic unit cell was predominant for times of exposure of the order of 10 4 h, while the tetragonal unit cell was more frequent upon prolonged ageing [ 31 ]. The FCC unit cell is regarded as an intermediate metastable crystal structure and is expected to be gradually replaced by the tetragonal unit cell of the Z-phase [ 30 , 31 ]. The relationship between the tetragonal and cubic unit cells in hybrid (FCC/Z-phase) particles is shown in Figure 1. Much effort has been devoted to investigations on nucleation, growth and chemical composition of this phase in martensitic (9–12) %Cr steels [ 32 – 37 ]. Chromium content plays a critical role in the driving force for the Z-phase precipitation. Detailed investigations proved that the dominant mechanism of the modified Z-phase formation is related to in situ transformation of (Nb,V)N particles into the FCC precursor by diffusion of chromium from the surroundings [ 30 , 32 , 35 , 36 ]. After the development of chromium rich regions at rims of the host MX particle, these regions consume vanadium, niobium and nitrogen from the dissolving MX particle. Experimental results are consistent with this mechanism of gradual conversion of MX precipitates via the FCC precursor rather than independent nucleation of Z-phase followed by dissolution of MX particles [ 30 , 32 ]. Final transformation of the FCC precursor to the tetragonal Z-phase is associated with ordering of solute atoms to produce the double layer structure which is typical for the tetragonal Z-phase [30,38]. Crystals 2023,13, 676 3 of 16 Crystals 2023, 13, x FOR PEER REVIEW 3 of 17 independent nucleation of Z-phase followed by dissolution of MX particles [30,32]. Final transformation of the FCC precursor to the tetragonal Z-phase is associated with ordering of solute atoms to produce the double layer structure which is typical for the tetragonal Z-phase [30,38]. Figure 1. The relationship between the tetragonal unit cell of the Z-phase and the FCC unit cell [29]. Vanadium is usually not reported in the nominal chemical composition of advanced austenitic steels. However, results of detailed chemical analyses prove that commercial heats of these steels often contain small amounts of vanadium. The presence of vanadium creates prerequisites for the partial substitution of niobium with vanadium in the particles of the Z-phase. A lack of information exists about precipitation behaviour of the modified Z-phase in austenitic steels containing both niobium and vanadium additions. Particles with the chemical composition corresponding to (Nb,V)CrN phase were observed after isothermal annealing at 750 °C/1170 h in an austenitic 18Cr-12Ni-VNbN steel in [39]. These particles were not reported as Z-phase because their crystal structure corresponded to FCC NaCl structure. Karlsson et al. [39] speculated that the particles with the FCC crystal structure could be a precursor of Z-phase. This paper deals with basic characteristics of the modified Z-phase in the AISI 316LN+Nb+V steel and in the HR3C steel. 2. Materials and Methods Chemical composition of a laboratory heated AISI 316LN+Nb+V steel is shown in Table 1. Preliminary heat treatment of forged rods with dimensions of ϕ12 × 125 mm consisted of solution annealing at 1300 °C for 0.5 h followed by quenching in water. Next, annealing of test samples was carried out at the temperature interval of 550 to 1250 °C with a step of 100 °C for 1, 20 and 50 h, followed by water quenching. Detailed microstructural characterization of annealed samples was performed. The results of minor phase identification were used for the construction of the TTP diagram of the modified Z-phase precipitation in the austenitic matrix. Table 1. Chemical composition of the AISI 316LN+Nb+V steel, wt.%. C S Mn Si P Cr Ni Mo V Nb N 0.03 0.007 1.44 0.59 0.017 18.10 12.50 2.44 0.25 0.11 0.16 Chemical composition of an industrial heat of the HR3C steel is shown in Table 2. As evident, a small amount of vanadium is present. Solution annealing of the tube ϕ42.8 × 6 mm was performed at 1250 °C for 2 min. The effect of thermal exposure on the Z-phase characteristics was studied on the sample that was annealed at 650 °C for 8600 h. Figure 1. The relationship between the tetragonal unit cell of the Z-phase and the FCC unit cell [ 29 ]. Vanadium is usually not reported in the nominal chemical composition of advanced austenitic steels. However, results of detailed chemical analyses prove that commercial heats of these steels often contain small amounts of vanadium. The presence of vanadium creates prerequisites for the partial substitution of niobium with vanadium in the particles of the Z-phase. A lack of information exists about precipitation behaviour of the modified Z-phase in austenitic steels containing both niobium and vanadium additions. Particles with the chemical composition corresponding to (Nb,V)CrN phase were observed after isothermal annealing at 750 ◦ C/1170 h in an austenitic 18Cr-12Ni-VNbN steel in [ 39 ]. These particles were not reported as Z-phase because their crystal structure corresponded to FCC NaCl structure. Karlsson et al. [39] speculated that the particles with the FCC crystal structure could be a precursor of Z-phase. This paper deals with basic characteristics of the modified Z-phase in the AISI 316LN+Nb+V steel and in the HR3C steel. 2. Materials and Methods Chemical composition of a laboratory heated AISI 316LN+Nb+V steel is shown in Table 1. Preliminary heat treatment of forged rods with dimensions of φ 12 × 125 mm consisted of solution annealing at 1300 ◦ C for 0.5 h followed by quenching in water. Next, annealing of test samples was carried out at the temperature interval of 550 to 1250 ◦ C with a step of 100 ◦ C for 1, 20 and 50 h, followed by water quenching. Detailed microstructural characterization of annealed samples was performed. The results of minor phase identification were used for the construction of the TTP diagram of the modified Z-phase precipitation in the austenitic matrix. Table 1. Chemical composition of the AISI 316LN+Nb+V steel, wt.%. C S Mn Si P Cr Ni Mo V Nb N 0.03 0.007 1.44 0.59 0.017 18.10 12.50 2.44 0.25 0.11 0.16 Chemical composition of an industrial heat of the HR3C steel is shown in Table 2. As evident, a small amount of vanadium is present. Solution annealing of the tube φ42.8 ×6 mm was performed at 1250 ◦ C for 2 min. The effect of thermal exposure on the Z-phase characteristics was studied on the sample that was annealed at 650 ◦C for 8600 h. Table 2. Chemical composition of the HR3C steel, wt.%. C S Mn Si P Cu Cr Ni Mo Nb V N 0.05 0.003 1.18 0.37 0.013 0.06 25.27 20.17 0.17 0.45 0.032 0.256 Crystals 2023,13, 676 4 of 16 Minor phase identification in the studied austenitic steels was performed using transmission electron microscopy (TEM). Both carbon extraction replicas and thin foils were used. Electron microscopy studies were performed on a JEM 2100 microscope (JEOL, Tokyo, Japan), equipped with INCA EDX system. The identification of minor phases was performed using a combination of selected area electron diffraction (SAED) and energydispersive X-ray microanalysis (EDX). The holder of the JEM 2100 microscope enabled double tilt in the range of angles x = ± 30 ◦ , y = ± 30 ◦ . SAED patterns at controlled tilt of the holder were obtained. Diffraction experiments revealed that Kikuchi patterns from (Nb,V)CrN particles in low index orientations are very similar to Kikuchi patterns of FCC crystals. This fact allowed for the use of the Kikuchi patterns of an FCC crystal for controlled navigation from one zone axis to another. Controlled tilting of particles into required orientations was very important in order to perform a reliable identification of the unit cell of particles investigated. The analysis was focused on attaining diffraction patterns exhibiting some reflections belonging solely to the tetragonal Z-phase, i.e., extra spots. Diffraction studies were accompanied by semiquantitative EDX microanalyses. Interstitial elements were not included into quantification of EDX spectra and results were normalized to 100%. The criterion applied for identification of the modified Z-phase was: 40 at.% < [Fe] + [Cr] < 70 at.% [ 5 , 40 ]. For preparation of carbon extraction replicas, etched metallographic samples were coated with a carbon layer with a thickness of 12 nm. Electrolytic etching in a 5% HCl solution in alcohol was applied to release the carbon film from the substrate. The carbon film with minor phase particles was stripped to the water surface, and after a rinse in water, pieces of carbon film were fished out on the backing grid. The thin foils were prepared by twin jet electropolishing in a solution of 5%HClO 4 in glacial acetic acid at room temperature and a voltage of 80 V. For reliable interpretation of experimental spot diffraction patterns, kinematical SAED patterns for both the tetragonal unit cell and the FCC unit cell were simulated using a computer programme. In calculations of kinematical intensities of Z-phase reflections, niobium atoms were replaced by vanadium, i.e., calculations were performed for VCrN phase. It was assumed that the positions of individual atoms in the unit cell were the same as those in the NbCrN phase [25]. Thermocalc software (Thermo-calc software, Stockholm, Sweden) and the TCFE 8 database were used for prediction of equilibrium minor phases in the steels investigated. Attention was paid to the effect of vanadium in the modified Z-phase on the solvus temperature of this phase in austenite. 3. Results 3.1. Simulation of Spot Diffraction Patterns The relationship among coordinate axes of the modified Zphase and the FCC precursor, see Figure 1, can be expressed as follows: [100]Z=1 21 * 10FCC ;[010]Z=1 2[110]FCC;[001]Z=cZ aFCC [001]FCC =1.83[001]FCC (1) These equations determine elements of transformation matrices which can be applied for transformation of Miller indexes of any vector → rin real space: hFCC,→ ri=(FCCTZ)hZ,→ ri hFCC,→ ri=  0.5 0.5 0 −0.5 0.5 0 0 0 1.83  hZ,→ ri(2) hZ,→ ri=(ZTFCC)hFCC,→ ri hZ,→ ri=  1−1 0 1 1 0 0 0 0.546  hFCC,→ ri(3) Crystals 2023,13, 676 5 of 16 For transformation of Miller indexes of vector → g in reciprocal space, the following transformation matrices can be used: hZ,→ gi∗=  0.5 −0.5 0 0.5 0.5 0 0 0 1.83  hFCC,→ gi∗hFCC,→ gi∗=  1 1 0 −1 1 0 0 0 0.546  hZ,→ gi∗(4) Transformation matrices were applied for calculations of all possible variants of diffraction patterns of the tetragonal unit cell of the Z-phase corresponding to the zone axes of the FCC precursor with low Miller indexes. The results of calculations for some low index zone axes are shown in Table 3. In some zone axes, the differences between the corresponding FCC and Z-phase diffraction patterns are so small that these zone axes should not be used to reliably distinguish between both phases by electron diffraction techniques. It means that in some zone axes all spots of the FCC phase are very close to Z-phase spots. Only in a limited number of Z-phase orientations are there extra spots in SAED patterns, i.e., spots belonging solely to the Z-phase. Such diffraction patterns make it possible to differentiate reliably between the tetragonal modified Z-phase and the FCC phase. As a rule, if the occurrence of some spots in diffraction patterns cannot be explained using the FCC unit cell, then the FCC unit cell is not the correct choice for interpretation of diffraction results. Figure 2a,b show the simulated diffraction patterns for zone axes [111] FCC and [041] Z , respectively. In the [041] Z zone axis there are extra spots which make it possible to uniquely distinguish between the tetragonal Z-phase and the FCC precursor. Table 3. Transformation of the FCC low index zone axes of the precursor into the tetragonal unit cell of the modified Z-phase. <uvw>FCC [uvw]FCC [uvw]ZExtra Spots * <100> [100] [110] Yes [001] [001] No <110> [110] [010] Yes [101] [221] No <111> [111] [041] Yes * the occurrence of extra spots in diffraction patterns of the tetragonal Z-phase. Crystals 2023, 13, x FOR PEER REVIEW 6 of 17 Figure 2. Simulated spot diffraction patterns: (a) zone axis [111]FCC, (b) zone axis [041]Z. 3.2. Investigations on the Modified Z-Phase in the AISI 316LN+Nb+V Steel TEM analysis of annealed samples revealed only two minor phases: MX and niobium, vanadium and chromium rich particles of the modified Z-phase. In samples annealed at 1250 °C neither MX nor modified Z-phase were present. It proved that preliminary heat treatment was carried out above the solvus temperature of these minor phases. Particles of MX and the modified Z-phase could not be distinguished on their morphology alone. Particles of MX phase were identified in all samples annealed in the temperature interval of 650–1150 °C. Figure 3 shows an MX particle in the sample after annealing at 1150 °C for 50 h. The average chemical composition of the MX phase at temperatures of 750, 950 and 1150 °C is shown in Table 4. Except for vanadium and niobium, particles of this phase also contained some chromium. The average content of chromium in the MX phase decreased with growing annealing temperature. Some MX particles exhibited needle-like morphology. The average size of MX particles decreased with decreasing temperature and time of annealing. MX particles decorated austenite grain boundaries and were also present inside austenite grains. Figure 4 shows intragranular precipitation of MX particles and the corresponding ring diffraction pattern in the sample annealed at 850 °C for 1 h. The lattice parameter of the FCC unit cell of the MX phase was determined as a = 4.19 nm. In all specimens investigated, MX particles constituted most precipitates. Figure 2. Simulated spot diffraction patterns: (a) zone axis [111]FCC, (b) zone axis [041]Z. Crystals 2023,13, 676 6 of 16 It is worth noting that in many cases simulated intensities of the extra spots are very weak, and therefore, it might be difficult to observe some of these spots in experimental diffraction patterns. Furthermore, simulated intensities of potentially overlapping spots of the tetragonal Z-phase and the FCC phase are not implicitly stronger than intensities of extra spots. The results of SAED simulations suggest that reliably distinguishing between the FCC and tetragonal unit cells under consideration requires a series of diffraction patterns obtained on each (Nb,V)CrN particle investigated. 3.2. Investigations on the Modified Z-Phase in the AISI 316LN+Nb+V Steel TEM analysis of annealed samples revealed only two minor phases: MX and niobium, vanadium and chromium rich particles of the modified Z-phase. In samples annealed at 1250 ◦ C neither MX nor modified Z-phase were present. It proved that preliminary heat treatment was carried out above the solvus temperature of these minor phases. Particles of MX and the modified Z-phase could not be distinguished on their morphology alone. Particles of MX phase were identified in all samples annealed in the temperature interval of 650–1150 ◦ C. Figure 3shows an MX particle in the sample after annealing at 1150 ◦ C for 50 h. The average chemical composition of the MX phase at temperatures of 750, 950 and 1150 ◦ C is shown in Table 4. Except for vanadium and niobium, particles of this phase also contained some chromium. The average content of chromium in the MX phase decreased with growing annealing temperature. Some MX particles exhibited needle-like morphology. The average size of MX particles decreased with decreasing temperature and time of annealing. MX particles decorated austenite grain boundaries and were also present inside austenite grains. Figure 4shows intragranular precipitation of MX particles and the corresponding ring diffraction pattern in the sample annealed at 850 ◦ C for 1 h. The lattice parameter of the FCC unit cell of the MX phase was determined as a = 4.19 nm. In all specimens investigated, MX particles constituted most precipitates. Crystals 2023, 13, x FOR PEER REVIEW 7 of 17 Figure 3. MX particle in the sample after annealing 1150 °C/50 h, bright field (BF) image; insert: zone axis [321]MX, carbon extraction replica. Table 4. Results of semiquantitative EDX analyses on MX particles; annealing time: 20 h, at.%. Temperature [°C] V Cr Nb 750 27.1 ± 1.8 37.3 ± 5.4 35.6 ± 6.3 950 44.5 ± 5.3 19.3 ± 3.9 36.2 ± 4.4 1150 36.2 ± 1.3 16.7 ± 1.5 49.1 ± 1.2 Figure 4. Intragranular precipitation after annealing 850 °C/1 h. (a) BF image, carbon extraction replica, (b) ring diffraction pattern of the MX phase ((Nb,V)N). Particles of the modified Z-phase were identified in the temperature interval of 750– 1050 °C. In this temperature range, particles of the modified Z-phase were present in all samples annealed for 20 and 50 h. At temperatures of 850 °C and 950 °C, particles of this minor phase were detected after holding time for one hour. Particles of the modified Zphase in some cases nucleated on MX particles (Figure 5a). Diffraction analysis revealed that the crystal structure of this particle corresponds to the tetragonal Z-phase. Figure 5c– Figure 3. MX particle in the sample after annealing 1150 ◦ C/50 h, bright field (BF) image; insert: zone axis [321]MX, carbon extraction replica. Table 4. Results of semiquantitative EDX analyses on MX particles; annealing time: 20 h, at.%. Temperature [◦C] V Cr Nb 750 27.1 ±1.8 37.3 ±5.4 35.6 ±6.3 950 44.5 ±5.3 19.3 ±3.9 36.2 ±4.4 1150 36.2 ±1.3 16.7 ±1.5 49.1 ±1.2 Crystals 2023,13, 676 7 of 16 Crystals 2023, 13, x FOR PEER REVIEW 7 of 17 Figure 3. MX particle in the sample after annealing 1150 °C/50 h, bright field (BF) image; insert: zone axis [321]MX, carbon extraction replica. Table 4. Results of semiquantitative EDX analyses on MX particles; annealing time: 20 h, at.%. Temperature [°C] V Cr Nb 750 27.1 ± 1.8 37.3 ± 5.4 35.6 ± 6.3 950 44.5 ± 5.3 19.3 ± 3.9 36.2 ± 4.4 1150 36.2 ± 1.3 16.7 ± 1.5 49.1 ± 1.2 Figure 4. Intragranular precipitation after annealing 850 °C/1 h. (a) BF image, carbon extraction replica, (b) ring diffraction pattern of the MX phase ((Nb,V)N). Particles of the modified Z-phase were identified in the temperature interval of 750– 1050 °C. In this temperature range, particles of the modified Z-phase were present in all samples annealed for 20 and 50 h. At temperatures of 850 °C and 950 °C, particles of this minor phase were detected after holding time for one hour. Particles of the modified Zphase in some cases nucleated on MX particles (Figure 5a). Diffraction analysis revealed that the crystal structure of this particle corresponds to the tetragonal Z-phase. Figure 5c– Figure 4. Intragranular precipitation after annealing 850 ◦ C/1 h. ( a ) BF image, carbon extraction replica, (b) ring diffraction pattern of the MX phase ((Nb,V)N). Particles of the modified Z-phase were identified in the temperature interval of 750–1050 ◦C. In this temperature range, particles of the modified Z-phase were present in all samples annealed for 20 and 50 h. At temperatures of 850 ◦ C and 950 ◦ C, particles of this minor phase were detected after holding time for one hour. Particles of the modified Z-phase in some cases nucleated on MX particles (Figure 5a). Diffraction analysis revealed that the crystal structure of this particle corresponds to the tetragonal Z-phase. Figure 5c–e show the SAED spot diffraction pattern and simulated diffraction patterns for [010] Z and [110] FCC of the FCC precursor, respectively. Due to extra spots in the diffraction pattern belonging to the tetragonal Z-phase, it is easy to discriminate between the tetragonal and FCC unit cells. Extra spots (in circles) in the SAED diffraction pattern prove that the crystal structure of the particle is tetragonal (Figure 5c,d). Streaking of reflections in the [001]* direction is probably related to defects on (001) atomic planes due to imperfect ordering of solute atoms in the double layer structure of the Z-phase. This effect was not observed in diffraction patterns on particles which precipitated at higher temperatures or longer holding times. Figure 5b shows the dark field (DF) image in the reflection 10− 2Z. Figure 6a shows intragranular precipitation in the sample annealed at 1050 ◦ C for 50 h, which was the maximum temperature for the formation of the modified Z-phase. Spot diffraction pattern in Figure 6b matches the simulated diffractogram in Figure 6c which belongs to the tetragonal unit cell of the Z-phase. The corresponding simulated diffraction pattern of the FCC phase is shown in Figure 6d. Particles of the modified Z-phase formed at 750 ◦ C showed the needle-like morphology (several nanometres in width and (50–100) nanometres in length). The average particle size increased with the annealing temperature and time. After annealing at 1050 ◦ C, particles of the modified Z-phase reached up to several hundreds of nanometres in length. More data are needed for evaluation of long-term dimensional stability of the (Nb,V)CrN phase in austenitic steels at temperatures for their engineering applications. Figure 7summarises results of investigations on the kinetics of the modified Z-phase formation in the temperature interval of 550–1250 ◦ C. The nose of the C-curve shows that the fastest precipitation of the modified Z-phase can be expected at approximately 900 ◦ C. The results of experimental studies indicate that the solvus temperature of the modified Z-phase in the AISI 316LN+Nb+V steel is approximately 1050 ◦C. Crystals 2023,13, 676 8 of 16 Crystals 2023, 13, x FOR PEER REVIEW 8 of 17 e show the SAED spot diffraction pattern and simulated diffraction patterns for [010]Z and [110]FCC of the FCC precursor, respectively. Due to extra spots in the diffraction pattern belonging to the tetragonal Z-phase, it is easy to discriminate between the tetragonal and FCC unit cells. Extra spots (in circles) in the SAED diffraction pattern prove that the crystal structure of the particle is tetragonal (Figure 5c,d). Streaking of reflections in the [001]* direction is probably related to defects on (001) atomic planes due to imperfect ordering of solute atoms in the double layer structure of the Z-phase. This effect was not observed in diffraction patterns on particles which precipitated at higher temperatures or longer holding times. Figure 5b shows the dark field (DF) image in the reflection 102 Z. Figure 6a shows intragranular precipitation in the sample annealed at 1050 °C for 50 h, which was the maximum temperature for the formation of the modified Z-phase. Spot diffraction pattern in Figure 6b matches the simulated diffractogram in Figure 6c which belongs to the tetragonal unit cell of the Z-phase. The corresponding simulated diffraction pattern of the FCC phase is shown in Figure 6d. Crystals 2023, 13, x FOR PEER REVIEW 9 of 17 Figure 5. Diffraction analysis of the Z-phase particle nucleated on the MX particle. (a) BF image, (b) DF image in 102 Z, (c) SAED pattern, (d) simulated spot diffraction pattern for zone axis [010]Z, (e) simulated diffraction pattern for zone axis [110]FCC. Particles of the modified Z-phase formed at 750 °C showed the needle-like morphology (several nanometres in width and (50–100) nanometres in length). The average particle size increased with the annealing temperature and time. After annealing at 1050 °C, particles of the modified Z-phase reached up to several hundreds of nanometres in length. More data are needed for evaluation of long-term dimensional stability of the (Nb,V)CrN phase in austenitic steels at temperatures for their engineering applications. Figure 5. Diffraction analysis of the Z-phase particle nucleated on the MX particle. ( a ) BF image, ( b ) DF image in 10 − 2Z , ( c ) SAED pattern, ( d ) simulated spot diffraction pattern for zone axis [010] Z , (e) simulated diffraction pattern for zone axis [110]FCC. Crystals 2023,13, 676 9 of 16 Crystals 2023, 13, x FOR PEER REVIEW 9 of 17 Figure 5. Diffraction analysis of the Z-phase particle nucleated on the MX particle. (a) BF image, (b) DF image in 102 Z, (c) SAED pattern, (d) simulated spot diffraction pattern for zone axis [010]Z, (e) simulated diffraction pattern for zone axis [110]FCC. Particles of the modified Z-phase formed at 750 °C showed the needle-like morphology (several nanometres in width and (50–100) nanometres in length). The average particle size increased with the annealing temperature and time. After annealing at 1050 °C, particles of the modified Z-phase reached up to several hundreds of nanometres in length. More data are needed for evaluation of long-term dimensional stability of the (Nb,V)CrN phase in austenitic steels at temperatures for their engineering applications. Crystals 2023, 13, x FOR PEER REVIEW 10 of 17 Figure 6. Analysis of the Z-phase particle in the sample after annealing 1050 °C/20 h. (a) Intragranular precipitation, BF image, carbon extraction replica, (b) spot diffraction pattern, (c) simulated diffraction pattern for the zone axis [021] Z , (d) simulated diffraction pattern for the zone axis [112] FCC . Figure 7 summarises results of investigations on the kinetics of the modified Z-phase formation in the temperature interval of 550–1250 °C. The nose of the C-curve shows that the fastest precipitation of the modified Z-phase can be expected at approximately 900 °C. The results of experimental studies indicate that the solvus temperature of the modified Z-phase in the AISI 316LN+Nb+V steel is approximately 1050 °C. Figure 7. TTP diagram of the modified Z-phase in the AISI 316LN+Nb+V steel. Results of semiquantitative EDX analyses of the modified Z-phase in samples annealed at temperatures in the range of 750–1050 °C for 20 h are summarized in Table 5. As the annealing temperature increases, the chromium content in the modified Z-phase decreases. Furthermore, the Nb/V ratio increases with increasing annealing temperature. Figure 6. Analysis of the Z-phase particle in the sample after annealing 1050 ◦ C/20 h. ( a ) Intragranular precipitation, BF image, carbon extraction replica, ( b ) spot diffraction pattern, ( c ) simulated diffraction pattern for the zone axis [021]Z, (d) simulated diffraction pattern for the zone axis [112]FCC. Crystals 2023, 13, x FOR PEER REVIEW 10 of 17 Figure 6. Analysis of the Z-phase particle in the sample after annealing 1050 °C/20 h. (a) Intragranular precipitation, BF image, carbon extraction replica, (b) spot diffraction pattern, (c) simulated diffraction pattern for the zone axis [021] Z , (d) simulated diffraction pattern for the zone axis [112] FCC . Figure 7 summarises results of investigations on the kinetics of the modified Z-phase formation in the temperature interval of 550–1250 °C. The nose of the C-curve shows that the fastest precipitation of the modified Z-phase can be expected at approximately 900 °C. The results of experimental studies indicate that the solvus temperature of the modified Z-phase in the AISI 316LN+Nb+V steel is approximately 1050 °C. Figure 7. TTP diagram of the modified Z-phase in the AISI 316LN+Nb+V steel. Results of semiquantitative EDX analyses of the modified Z-phase in samples annealed at temperatures in the range of 750–1050 °C for 20 h are summarized in Table 5. As the annealing temperature increases, the chromium content in the modified Z-phase decreases. Furthermore, the Nb/V ratio increases with increasing annealing temperature. Figure 7. TTP diagram of the modified Z-phase in the AISI 316LN+Nb+V steel. Crystals 2023,13, 676 16 of 16 27. Strang, A.; Vodárek, V. Precipitation in martensitic 12CrMoVNb steels during high temperature creep. In Microstructural Development and Stability in High Chromium Ferritic Power Plant Steels; Strang, A., Gooch, D.J., Eds.; Maney Publishing: London, UK, 1997. 28. Sawada, K.; Kimura, K.; Tabuchi, M. TTP diagrams of Z phase in 9-12%Cr heat-resistant steels. ISIJ Int. 2007 ,47, 733–739. [CrossRef] 29. Danielsen, H.K.; Hald, J.; Grumsen, F.B.; Somers, A.J. On the crystal structure of Z-phase Cr(V,Nb)N. Metall. Mater. Trans. A 2006 , 37, 2633–2640. [CrossRef] 30. Danielsen, H.K.; Hald, J. Behaviour of Z-phase in 9–12%Cr steels. Energy Mater. 2006,1, 49–57. [CrossRef] 31. Vodárek, V.; Danielsen, H.K.; Grumsen, F.B.; Hald, J.; Strang, A. Electron Diffraction Studies on Nb(V)CrN Particles in 12CrMoVNbN Steels. In Proceedings of the 8th Liege Conference on Materials for Advanced Power Engineering, Liege, Belgium, 18–20 September 2006; Forschungszentrum Jülich GmbH: Jülich, Germany, 2006; pp. 1251–1260. 32. Cipolla, L.; Danielsen, H.K.; Venditti, D.; Di Nunzio, P.E.; Hald, J.; Somers, A.J. Conversion of MX nitrides to modified Z-phase in a 12%Cr steel. Acta Mater. 2010,58, 669–679. [CrossRef] 33. Sawada, K.; Kushima, H.; Kimura, K.; Tabuchi, M. Z-phase formation during creep and aging in 9–12% Cr heat resistant steels. ISIJ Int. 2006,46, 769–775. [CrossRef] 34. Vodárek, V.; Strang, A. Z phase precipitation in martensitic 12CrMoVNb steels. J. Phys. IV. 2003,112, 445–448. [CrossRef] 35. Danielsen, H.K.; Hald, J. On the nucleation and dissolution process of Z-phase Cr(V,Nb)N in martensitic 12% Cr steels. Mater. Sci. Eng. A 2009,505, 169–177. [CrossRef] 36. Cipolla, L.; Danielsen, H.K.; Di Nunzio, P.E.; Venditti, D.; Hald, J.; Somers, M.A.J. On the role of Nb in Z-phase formation in a 12%Cr steel. Scr. Mater. 2010,63, 324–327. [CrossRef] 37. Vodárek, V.; Strang, A. Compositional changes in minor phases present in 12CrMoN steels during thermal exposure at 550 degrees C. Mater. Sci. Technol. 2000,16, 1207–1213. [CrossRef] 38. Danielsen, H.K.; Hald, J.; Somers, M.A.J. Atomic Resolution imaging of precipitate transformation from cubic TaN to tetragonal CrTaN. Scr. Mater. 2012,66, 261–264. 39. Karlsson, L.; Henjered, A.; Andrén, H.O.; Nordén, H. Composition and crystallography of nitride precipitates in an austenitic stainless steel containing niobium and vanadium. Mater. Sci. Technol. 1985,1, 337–343. [CrossRef] 40. Holešinský, J. Structural Stability and Heat Resistance of Steels for Applications in the Energy Industry. Dissertation Thesis, VSB-Technical University of Ostrava, Ostrava, Czech Republic, 2015. (In Czech) Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.