Nanostructured electrospun fibers with self-assembled cyclo-L-Tryptophan-L-Tyrosine dipeptide as piezoelectric materials and optical sd harmonic generators

Citation: Santos, D.; Baptista, R.M.F.; Handa, A.; Almeida, B.; Rodrigues, P.V.; Castro, C.; Machado, A.; Rodrigues, M.J.L.F.; Belsley, M.; de Matos Gomes, E. Nanostructured Electrospun Fibers with Self-Assembled Cyclo-L-TryptophanL-Tyrosine Dipeptide as Piezoelectric Materials and Optical Second Harmonic Generators. Materials 2023, 16, 4993. https://doi.org/10.3390/ ma16144993 Academic Editors: Nader Shehata, Islam Shyha and Ahmed H. Hassanin Received: 20 June 2023 Revised: 7 July 2023 Accepted: 11 July 2023 Published: 14 July 2023 Copyright: © 2023 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https:// creativecommons.org/licenses/by/ 4.0/). materials Article Nanostructured Electrospun Fibers with Self-Assembled Cyclo-L-Tryptophan-L-Tyrosine Dipeptide as Piezoelectric Materials and Optical Second Harmonic Generators Daniela Santos 1, Rosa M. F. Baptista 1,* , Adelino Handa 1, Bernardo Almeida 1, Pedro V. Rodrigues 2, Cidália Castro 2, Ana Machado 2,* , Manuel J. L. F. Rodrigues 1, Michael Belsley 1 and Etelvina de Matos Gomes 1 1Laboratory for Materials and Emergent Technologies (LAPMET), Centre of Physics of Minho and Porto Universities (CF-UM-UP), University of Minho, Campus de Gualtar, 4710-057 Braga, Portugal; [email protected] (D.S.); [email protected] (A.H.); [email protected] (B.A.); [email protected] (M.J.L.F.R.); [email protected] (M.B.); [email protected] (E.d.M.G.) 2Institute for Polymers and Composites, University of Minho, Campus de Gualtar, 4800-058 Guimarães, Portugal ; pedro.r[email protected] (P.V.R.); [email protected] (C.C.) *Correspondence: [email protected] (R.M.F.B.); [email protected] (A.M.) Abstract: The potential use of nanostructured dipeptide self-assemblies in materials science for energy harvesting devices is a highly sought-after area of research. Specifically, aromatic cyclodipeptides containing tryptophan have garnered attention due to their wide-bandgap semiconductor properties, high mechanical rigidity, photoluminescence, and nonlinear optical behavior. In this study, we present the development of a hybrid system comprising biopolymer electrospun fibers incorporated with the chiral cyclo-dipeptide L-Tryptophan-L-Tyrosine. The resulting nanofibers are wide-bandgap semiconductors (bandgap energy 4.0 eV) consisting of self-assembled nanotubes embedded within a polymer matrix, exhibiting intense blue photoluminescence. Moreover, the cyclodipeptide L-Tryptophan-L-Tyrosine incorporated into polycaprolactone nanofibers displays a strong effective second harmonic generation signal of 0.36 pm/V and shows notable piezoelectric properties with a high effective coefficient of 22 pCN −1 , a piezoelectric voltage coefficient of ge f f = 1.2 VmN −1 and a peak power density delivered by the nanofiber mat of 0.16 µ Wcm −2 . These hybrid systems hold great promise for applications in the field of nanoenergy harvesting and nanophotonics. Keywords: cyclo-dipeptide; electrospinning; piezoelectricity; nanofibers; optical second harmonic generation; self-assembly 1. Introduction Nanotechnology has significantly impacted various industries, including bionanotechnology. It has advanced medical imaging, targeted drug delivery, customized medical devices, and disease-specific therapeutics [1] . In energy generation and storage, nanotechnology has improved efficiency and sustainability [2] . Additionally, bionanotechnology has led to the creation of novel materials and sensors for the detection and removal of environmental pollutants [3]. Peptides, consisting of short amino acid chains, exhibit diverse structures, functions, and biological activities [4] . Among them, cyclic dipeptides or cyclo-dipeptides (CDPs) are notable. CDPs form ring structures through peptide bonds and possess enhanced bioactivity, structural rigidity, biofunctionalization, and enzymatic stability. These unique characteristics make CDPs promising for various bionanotechnology applications [5,6]. CDPs exhibit antimicrobial and anticancer properties. They can self-assemble into nanostructures like nanotubes, nanofibers, nanowires, and nanospheres, offering unique properties based on their sequence and environment [7]. Materials 2023,16, 4993. https://doi.org/10.3390/ma16144993 https://www.mdpi.com/journal/materials Materials 2023,16, 4993 2 of 17 Through engineering, CDPs self-assemble into nanoscale structures such as nanotubes, nanofibers, nanowires, and nanospheres with unique properties [8,9] . Aromatic groups in organic materials, including dipeptide nanostructures, exhibit enhanced rigidity and mechanical, optical, and piezoelectric properties when self-assembled [10,11]. Self-assembly occurs through non-covalent interactions such as hydrogen bonding, electrostatic interactions, Van der Waals forces, π - π and hydrophobic interactions [12] . Combining CDPs with other nanomaterials and technologies enables the creation of novel materials and devices applicable in tissue engineering, drug delivery, biosensors, and diagnostics [6,8,9,13] . CDPs, particularly those containing tryptophan, self-assemble through supramolecular phases involving hydrogen bonding and aromatic interactions, resulting in improved conductivity, photoluminescence, mechanical strength, and piezoelectric properties [8,13–15] . Incorporating cyclic dipeptides into polymer fibers enhances mechanical properties, making them suitable for composite materials, the manufacturing of microelectronic devices, and tissue engineering [16] . Electrospinning, a technique utilizing electrostatic forces, can be employed to create fibers incorporating CDPs within a polymeric matrix. Factors such as polymer solution properties, flow rate, electric field strength, needle-to-collector distance, and environmental conditions influence the electrospinning process, affecting fiber morphology and diameter. Controlling these factors is crucial to optimizing nanofiber performance [17,18]. Studying second harmonic generation and piezoelectric properties in hybrid systems with cyclic dipeptides is vital for creating advanced materials and devices in various fields. Second harmonic generation is a nonlinear optical property that allows for the efficient conversion of a single light beam into two photons of higher energy [19–21] . Piezoelectricity, on the other hand, involves the generation of electric charge under mechanical stress and is essential in pressure sensors, mechanical energy devices, and energy conversion systems [22]. Exploring and understanding these properties in cyclic dipeptide-incorporated fiber systems can lead to the development of innovative materials. This study represents an innovative contribution in the field, as it is the first time that Cyclo-L-Tryptophan-L-Tyrosine dipeptides have been integrated into a fibrous matrix. We used the electrospinning technique to promote the immediate self-assembling of nanostructures within the fibers. As a result, we achieved a nanofibrous structure with piezoelectric and optical second harmonic generation properties. It is important to emphasize that self-assembling is typically reported in solution, making this approach particularly innovative. 2. Materials and Methods 2.1. Materials The chiral cyclic dipeptide Cyclo-L-Tryptophan-L-Tyrosine, hereafter referred to as Cyclo(L-Trp-L-Tyr) (Mw = 349.39 g/mol), was purchased from Bachem AG (Bubendorf, Switzerland), and its chemical formula is represented in Figure 1. The biopolymer chosen was polycaprolactone (PCL, Mw = 80,000 g/mol) purchased from Sigma-Aldrich (Darmstadt, Germany). Its chemical formula is also illustrated in Figure 1. Regarding the solvents used, 1,1,1,3,3,3-hexafluoro-2-propanol (HFP), dichloromethane (DCM), N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMAc) and methanol (MeOH), they were purchased from Merck/Sigma-Aldrich (Darmstadt, Germany). All chemicals were used as received. 2.2. Dipeptide Self-Assembled Nanostructures in Solution To visualize the nanostructures to which the dipeptide self-assembles, a solution was prepared by dissolving 0.80 mg of Cyclo(L-Trp-L-Tyr) in the following mixture of solvents: 4:2:1 DMF/DMAc/H 2 O. This solution was filtered with a membrane with a 0.45 µ m pore diameter and allowed to grow the nanostructures for a month. A drop of this solution was Materials 2023,16, 4993 3 of 17 then placed on a silica slide, and the solvents were slowly evaporated at room temperature and sent for scanning electron microscopy (SEM) analysis. To study the optical absorption and photoluminescence spectra, the dipeptide was dissolved in HFP at a concentration of 100 mg/mL. Afterwards, it was diluted in MeOH to the final concentrations depending on the characterization and left at room temperature for 24 h. 2.3. Electrospinning of Nanofibers For electrospinning, a 10% polymer solution of PCL (w/v) was completely dissolved in DCM at 300 rpm and 35 ° C. A mixture of solvents DMF/DMAc was used to dissolve Cyclo(L-Trp-L-Tyr) in a 1:5 w/w. This was incorporated into the polymer solution, resulting in a 4:1:1 volume ratio of solvents. At room temperature and for several hours, the obtained solution was stirred at 300 rpm. The vertical electrospinning used, under ambient conditions, has a high voltage power supply with an electrical potential difference of 18 kV, from Spellmann CZE2000, Bochum, Germany. The tip-of-needle collector distance (TCD) was 11 cm, and a high purity aluminum foil was placed on the collector to facilitate fiber manipulation and act as an electrode. Other electrospinning parameters to ensure a stable process and the production of bead-free nanofibers were the flow rate of 0.18 mL/h and a needle with an outer diameter of 0.813 mm (inner diameter 0.508 mm). The syringe was loaded with the polymeric and dipeptide solution and the high voltage power of 18 kV was applied to the tip of needle, as seen in Figure 1. V + + + + ++ ++ + ++ ++ Taylor Cone N H H NO O OH HN Self-assembly Cyclo(L-Trp-L-Tyr) Cyclo(L-Trp-L-Tyr) Nanofibrils PCL Figure 1. Schematic representation of the electrospinning process and the materials used, both in the production of the Cyclo(L-Trp-L-Tyr)@PCL nanofibers and the self-assembly in solution of dipeptide. 2.4. Scanning Electron Microscopy (SEM) The morphological characterization of the dipeptide was investigated using SEM. This analytical technique not only enables the identification of the nanostructures that the CDP self-assembles into, but also allows for the examination of their size distribution. The primary objective of this study is to investigate and compare the nanostructures formed in solution with those formed during the process of electrospinning within the polymeric matrix. Materials 2023,16, 4993 4 of 17 To study the morphology of Cyclo(L-Trp-L-Tyr) structures, scanning electron microscopy was performed using a Nova Nano SEM 200 microscope, operated at an accelerating voltage of 10 kV. Slides with Cyclo(L-Trp-L-Tyr) structures in solution and the fiber mat were covered with a 10 nm thick Au-Pd (gold–lead) film (80–20 weight%) using a high resolution sputter coater, 208HR Cressington Company, coupled to a high resolution thickness controller, MTM-20 Cressigton. The resulting images were analyzed using ImageJ 1.53 k image analysis software (NIH, https://imagej.nih.gov/ij/, 13 February 2023). The distribution and average diameters were calculated by measuring 145 nanofibrils and 88 fibers from the SEM images, and the results were fitted to a log-normal function. 2.5. Confocal Laser Scanning Microscopy By employing this photoluminescent technique, it becomes possible to observe the distribution of the active material (CDP) in the interior of the nanofibers. The Olympus ™ FluoView FV1000 confocal scanning laser microscope (Olympus, Tokyo, Japan) was used to observe the fluorescence of the nanofibers with a 40 × objective, an excitation wavelength of 405 nm and detection filters BA 430–470. Confocal images were acquired with a 800 × 800 pixel resolution and a 1 cm 2 fiber mat with a 120 µ m thickness on a glass slide. The sample was scanned at room temperature. 2.6. Optical Absorption, Photoluminescence and Diffuse Reflectance Spectroscopy (DRS) The optical characterization of the fibers using techniques such as optical absorption, photoluminescence, and diffuse reflectance spectroscopy is crucial for understanding their electronic and optical properties. These techniques enable the determination of the bandgap, which is essential for evaluating the semiconducting properties of the fibers and their potential in optical and electronic applications. Optical absorption (OA) measurements were performed on Cyclo(L-Trp-L-Tyr) solutions and fiber mat using a Shimadzu UV-3600 Plus UV–Vis–NIR (ultraviolet/visible/nearinfrared) spectrophotometer (Shimadzu Corporation, Kyoto, Japan). At room temperature and in the wavelength range of 200 to 600 nm, the solutions were prepared in methanol and measured in a quartz cuvette with a path length of 1 cm. From UV–vis absorption spectroscopy, it is possible to determine the optical bandgap energy (Eg) of the nanoparticles using the Tauc plot given by (αhν)n=k(hν−Eg) [ 23 ]. The parameters are the following: α is the absorption coefficient; hν is the incident photon energy; n, is the type of electronic transition and, for this work, n= 1 / 2, as this is an indirect bandgap material; kis a constant of proportionality independent of the energy and k=1 (amorphous materials). The equipment used for the photoluminescence (PL) spectra was a Fluorolog 3 spectrofluorimeter (HORIBA Jobin Yvon IBH Ltd., Glasgow, UK) using an excitation wavelength of 280 nm and in the wavelength range of 290 to 600 nm, with input and output slits fixed to provide a spectral resolution of 2 nm. Photoluminescence excitation (PLE) spectra were recorded in the wavelength range of 220 to 300 nm. For the measurement of the diffuse reflectance spectrum (DRS) of the nanofiber mat, a UV2501PC spectrophotometer (Shimadzu Corporation, Kyoto, Japan) equipped with an integration sphere, Shimadzu ISR-205 240A, was used, and barium sulfate was taken as a reference. In the measurement, a wavelength rate of 200 to 800 nm was used with a step size of 1 nm. To determine the bandgap energy (Eg) of the material, we applied the Kulbelka–Munk function, F(R), to the experimental data obtained from DRS analysis [24] . The Kubelka–Munk function is given by F(R) = ( 1 −R)2/ 2 R , where R is the total reflectance coefficient of the material. As such, the bandgap is calculated using equation [hνF(R)]1/2 =α(hν−Eg) [ 25 ]. 2.7. Mechanical and Hydrophobic Tests The mechanical and hydrophobic characterization of the fibers is essential for their application as piezoelectric nanogenerators. Through the measurement of mechanical properties such as tensile strength and elastic modulus, we can determine their capacity to Materials 2023,16, 4993 5 of 17 generate piezoelectric energy under mechanical stress, which is crucial for the operation of the nanogenerators. Additionally, the characterization of fiber hydrophobicity through contact angle measurements is relevant for applications in humid environments, ensuring the efficiency and stability of piezoelectric nanogenerators. Mechanical tests were performed on a Zwick/Roell Z005 (ZwickRoell, Ulm, Germany) universal testing machine (ASTM D882-02). The specimens were cut from electrospun PCL fiber mats (40 × 10 mm) and tested at 25 mm/min with a gauge length of 26 mm. The mechanical indexes are the average values of at least 7 specimens. The hydrophilicity of the electrospun PCL fiber mat was measured using a goniometer (Contact Angle System OCA 20 Dataphysics, Filderstadt, Germany). Deionized water (3 µL) was automatically dropped onto the flat fibers with a precision syringe, following the sessile drop method. At least 20 measurements were made and the mean value was taken. 2.8. Second Harmonic Generation (SHG) To enhance the characterization of the optical properties of the fibrous material, analyze the crystalline structures of the nanostructures within the fibers, and evaluate nonlinear processes, comprehensive studies of second harmonic generation were conducted. Second harmonic measurements on the fiber mats were performed using a modelocked Ti: Sapphire laser (Coherent Mira) as an excitation source. The incident fundamental light was focused on the fiber mats using a Nikon CFI Plan Fluor × 10 objective; see Figure 2. Due to the opacity of the fiber mats, the second harmonic light was detected in reflection (epi-illumination). Although the bandwidth of the fundamental light is sufficient to produce 85 fs pulses (full-width half-maximum), we estimate that dispersion in the optical elements stretches the pulses to an approximately 120 fs duration when incident on the samples. For the fibers, incident pulse energies ranged from 65 to 130 pJ. A 1 mm thick beta barium borate (BBO) crystal cut for phase matching at 800 nm was used to calibrate the detection system. For the BBO crystal, the incident pulse energies were 5 to 7 pJ. The second harmonic light was separated from the incident fundamental light by a short-pass dichroic mirror; then, it passed through a narrow band-pass filter (Semrock FF01-405/150-25) before being focused onto a fiber bundle coupled to an Andor imaging spectrometer (Shamrock 300i) equipped with a charge-coupled device, CCD, array (Newton) cooled to − 50 ◦ C. The signal was integrated for 1 s in the case of the fibers and 4 ms in the case of BBO. The second harmonic spectra were fit to a Gaussian profile as detailed in the supplementary information of [ 26 ]. The area under the Gaussian fit was taken as a proxy for the total number of second harmonic signal counts. 800 nm 120 fs 80 MHz PBS λ/2 10× Dichroic mirror Shortpass Spectrometer Shortpass filter Sample Lens Figure 2. Second harmonic microscope layout. PBS—Polarized beam splitter; λ /2—half-waveplate. The transmission of the PBS is aligned vertically. Materials 2023,16, 4993 6 of 17 2.9. Piezoelectric Measurements The measurements of the piezoelectric properties were conducted using a well-defined experimental setup (see Figure S1). This setup ensured accurate and reliable measurements, which are essential for validating and reproducing the results obtained for the piezoelectric properties of the fibers. The piezoelectric output voltage was measured through a load resistance of 100 M Ω and collected in a digital storage oscilloscope (Agilent Technologies DS0-X-3012A3012A, Waldbronn, Germany) after going through a low-pass filter and a low noise preamplifier (Research systems SR560, Stanford Research Systems, Stanford, CA, USA). The nanofiber sample had a 30 × 40 mm 2 area and a thickness of 120 µ m and was placed in thin plates of high-purity copper (top: 23 × 30 mm 2 and bottom: 30 × 33 mm 2 ). Periodic mechanical forces were applied to the fiber array by a vibration generator (Frederiksen SF2185) with a frequency of 3 Hz determined by a signal generator (Hewlett Packard 33120A). Before measuring, it was necessary to calibrate the applied forces with a FSR402 force-sensing resistor (Interlink Electronics Sensor Technology, Graefelfing, Germany). The forces applied were uniform and perpendicular to the surface area of the sample. 3. Results and Discussion 3.1. Morphological Characterization The dipeptide Cyclo(L-Trp-L-Tyr) in a solution of DMF/DMAc/H 2 O self-assembles into nanofibrils, as may be seen in the SEM images in Figure 3a,b. These nanofibrils have an average diameter of 218 ± 70 nm as shown in Figure 3c. The histogram was constructed from a total of 145 measurements, with the minimum diameter of 87 nm and the maximum diameter of 487 nm. Figure 3d,e are the SEM images of the dipeptide embedded into nanofibers, Cyclo(LTrp-L-Tyr)@PCL, fabricated by the electrospinning technique. These fibers have an average diameter of 417 ± 112 nm and a quite wide diameter distribution from a minimum diameter of 208 nm to a maximum of 696 nm, Figure 3f. In Figure 3e, it is possible to see nanotubes formed outside the fiber, with an average diameter of 58 ± 13 nm, indicating that in the polymer matrix, the dipeptide self-assembles in the form of nanotubes. In hydrogel form, You Y. and co-authors successfully produced Cyclo(L-Trp-L-Tyr) dipeptide fibrils measuring 100 ± 50 nm in width. Furthermore, they observed interconnected fibrous networks in 3D, formed by these fibrils [27]. In our previous work [ 16 ], we verified that the dipeptide Cyclo(L-Trp-L-Trp) selfassembles into nanospheres with an average diameter of 245 nm. In the current study, we utilized the dipeptide Cyclo(L-Trp-L-Tyr), taking advantage of the tyrosine OH group’s ability to form additional hydrogen bonds with both the tryptophan units and within the tyrosine residues. These hydrogen bonds, facilitated by the tyrosine OH group, are considered stronger than those formed by the tryptophan NH group. This increased strength is attributed to the higher electronegativity of oxygen in the tyrosine OH group compared to nitrogen in the tryptophan NH group, resulting in a greater attraction of shared electrons within the hydrogen bond [27,28] . Furthermore, the linear arrangement of the hydroxyl (OH) group in tyrosine contributes to enhanced interactions. This is due to the electron-withdrawing nature of the hydroxyl substitution on the phenyl side chain of tyrosine, promoting more efficient π - π interactions involving the side chains [ 29 ]. Additionally, it is important to note that tryptophan exhibits a higher hydrophobicity index (1.9) compared to tyrosine ( − 0.7) [30] . These differences in hydrophobicity may play a role in the self-assembling process. When combined with the enhanced strength of the hydrogen bonds, they facilitate the formation of a more extensive and organized network, thus promoting the formation of nanotubes. In terms of electrospun nanofibers, they showed no bead formation, and electrospinning proved to be a stable and appropriate technique for the production of these nanomaterials. In article [ 16 ], we obtained an average diameter of 600 nm for PCL nanofibers functionalized with Cyclo(L-Trp-L-Trp), and in [ 31 ], the electrospun fibers of Boc-Phe-Phe Materials 2023,16, 4993 7 of 17 (Boc-L-phenylalanine-L-phenylalanine-OH) formed from PCL resulted in diameters in a range of 590–700 nm, similar to the results from the present study. An additional structural characterization was performed by Fourier transform infrared spectroscopy (FTIR); see Figure S2. The spectra show changes in peak intensity and shape, indicating the successful incorporation of the CDP inside the fibers. 40 μm (a) (d) 20 μm 1 μm (b) 1 μm (e) Figure 3. SEM images of Cyclo(L-Trp-L-Tyr): ( a , b ) as self-assembled nanofibrils in a solution of DMF/DMAc/H 2 O at a magnification of 2500 × and 50,000 × , respectively; ( d , e ) as nanofibers produced by electrospinning with Cyclo(L-Trp-L-Tyr) embedded into the biopolymer PCL at a magnification of 5000 × and 100,000 × . The respective diameter histograms of the nanofibrils ( c ) and the nanofibers (f) are represented with dashed curves, indicating lognormal distributions. Materials 2023,16, 4993 8 of 17 3.2. Optical Absorption, Photoluminescence and Diffuse Reflectance Spectroscopy of Dipeptide Self-Assemblies The UV–vis absorption spectrum of a 0.43 mM Cyclo(L-Trp-L-Tyr) in methanol is depicted in Figure 4a, showing an absorption band from 250 to 300 nm with three smaller spikes at 273, 280 and 289 nm. These represent the formation of structures called quantum dots, QDs. As reported in the literature, for the case of Cyclo-FW (cyclo-phenylalanine–tryptophan) and Cyclo-WW (cyclo-tryptophan–tryptophan), the monomers of CDPs form dimeric QDs that act as the foundation for more complex supramolecular structures [8]. The bandgap energy of Eg= 4.11 ± 0.01 eV was obtained for Cyclo(L-Trp-L-Tyr) from the absorption spectrum through the Tauc plot; see the inset in Figure 4a. The obtained value agrees with those reported from density functional theory (DFT) for Cyclo-FW and Cyclo-WW, which have bandgap energies of 3.63 eV and 3.56 eV, respectively [8]. In Figure 4b, it is possible to verify the match between the absorption spectrum and the photoluminescence excitation (PLE) spectrum of the dipeptide in solution for excitation at a maximum wavelength of 280 nm. The photoluminescence (PL) emission spectrum of the 0.001 mM dipeptide solution in MeOH for excitation at 280 nm is represented in Figure 4b with maximum emission peak at 311 nm. The PL spectrum of Cyclo(L-Trp-L-Tyr)@PCL nanofibers is represented in blue, also in Figure 4b, with a maximum at 330 nm and another, less intense emission peak at 440 nm, in the blue region of the optical spectra. That might indicate the presence of larger dipeptide nanostructures. The shift observed in the PL spectrum, from 311 nm for a dipeptide solution to 330 nm when the dipeptide is embedded into the nanofiber, is representative of an increase in the size of the nanostructures incorporated into the nanofibers. As a further study of the nanofibers, the diffuse reflectance spectrum (DRS) was measured for Cyclo(L-Trp-L-Tyr)@PCL and compared with the fiber mat without the embedded dipeptide in Figure 4c. The spectrum shows two peaks of minimum reflectance at 283 and 330 nm. The bandgap energies obtained for the dipeptide nanostructures both in solution and embedded into the electrospun fibers are approximately 4.0 eV, which are expected values for organic wide-bandgap semiconductors [32]. The bandgap energy values obtained in this study for Cyclo(L-Trp-L-Tyr) are also similar to those reported in a previous work with Cyclo(L-Trp-L-Trp) in solution and in fibers [16]. In Figure 4d, the confocal microscopy image of Cyclo(L-Trp-L-Tyr)@PCL nanofibers is presenting, showing intense blue photoluminescence due to CDP nanostructures in the interior of the fibers. (a) (b) Figure 4. Cont. Materials 2023,16, 4993 9 of 17 300 400 500 600 700 800 10 20 30 40 50 60 70 80 90 100 110 3.0 3.5 4.0 4.5 5.0 0.0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 (F(R)hν)1/2 (eV)1/2 Energy (eV) Cyclo(L-Trp-L-Tyr)@PCL Linear Fit Eg= 3.997 �0.003 eV Reflectance (%) Wavelength (nm) PCL Cyclo(L-Trp-L-Tyr)@PCL (c) (d) Figure 4. ( a ) Normalized UV–vis absorption spectrum with the bandgap energy obtained from the calculation of the Tauc plot (inset). ( b ) Normalized UV–vis absorption, photoluminescence excitation (PLE), photoluminescence (PL) of Cyclo(L-Trp-L-Tyr) in MeOH and PL spectra of Cyclo(L-Trp-LTyr)@PCL nanofibers. ( c ) DRS of Cyclo(L-Trp-L-Tyr)@PCL inset represents the bandgap obtained from the Kubelka–Munk function. ( d ) Confocal microscopy image of the Cyclo(L-Trp-L-Tyr)@PCL nanofiber mat under a laser excitation of 405 nm. 3.3. Mechanical and Hydrophobic Properties of Electrospun Fibers In Figure 5, the mechanical properties of PCL fibers are presented, with stress–strain curves indicating that the incorporation of CDPs increases stiffness. On average, the elastic modulus (Young’s modulus) increased by 445% (from 6.9 to 37.6 MPa) and the tensile strength increased by 72% (from 1.5 to 2.6 MPa), while the elongation at break was reduced by 35% (from 121 to 79%). Additionally, in a previous study, a notable improvement in the mechanical characteristics of the polymer was observed with the integration of organic crystals, specifically involving polyvinyl chloride (PVC) [33]. The cyclo-dipeptides effectively transfer applied forces between the polymer and nanotubes, reinforcing the polymeric matrix. This behavior is similar to that observed for electrospun polymer fibers embedded with nanospheres of the Cyclo(L-Trp-L-Trp) dipeptide [ 16 ] where the fiber mechanical properties were improved. These results, an increase in the elastic modulus and an elongation at break, are beneficial to the piezoelectric response of the material, enabling the fiber mat to withstand greater forces and deformations. Young’s modulus was found to depend significantly on the angle between the stretch direction and the fiber direction [ 34 ]; in our case, the functional electrospun fibers were stretched along the longitudinal axis of the fiber. Our previous work also demonstrates that the incorporation of lead-free organic ferroelectric perovskite N-methyl-N’-diazabicyclo [2.2.2]octonium-ammonium triiodide (MDABCO-NH 4 I 3 ) nanocrystals in polyvinyl chloride microfibers [ 33 ] resulted in an improvement in Young’s modulus compared to polymer electrospun fibers with no embedded material, as shown in Table 1. Materials 2023,16, 4993 16 of 17 3. Taran, M.; Safaei, M.; Karimi, N.; Almasi, A. Benefits and Application of Nanotechnology in Environmental Science: An Overview. Biointerface Res. Appl. Chem. 2020,11, 7860–7870. [CrossRef] 4. Gazit, E. Self-Assembled Peptide Nanostructures: The Design of Molecular Building Blocks and Their Technological Utilization. Chem. Soc. Rev. 2007,36, 1263. [CrossRef] [PubMed] 5. Manchineella, S.; Govindaraju, T. Molecular Self-Assembly of Cyclic Dipeptide Derivatives and Their Applications. ChemPlusChem 2017,82, 88–106. [CrossRef] [PubMed] 6. Chen, Y.; Tao, K.; Ji, W.; Makam, P.; Rencus-Lazar, S.; Gazit, E. Self-Assembly of Cyclic Dipeptides: Platforms for Functional Materials. Protein Peptide Lett. 2020,27, 688–697. [CrossRef] 7. Zhao, K.; Xing, R.; Yan, X. Cyclic Dipeptides: Biological Activities and Self-assembled Materials. Peptide Sci. 2021 ,113. [CrossRef] 8. Tao, K.; Fan, Z.; Sun, L.; Makam, P.; Tian, Z.; Ruegsegger, M.; Shaham-Niv, S.; Hansford, D.; Aizen, R.; Pan, Z.; et al. Quantum Confined Peptide Assemblies with Tunable Visible to Near-Infrared Spectral Range. Nat. Commun. 2018,9, 3217. [CrossRef] 9. Jeziorna, A.; Stopczyk, K.; Skorupska, E.; Luberda-Durnas, K.; Oszajca, M.; Lasocha, W.; Górecki, M.; Frelek, J.; Potrzebowski, M.J. Cyclic Dipeptides as Building Units of Nanoand Microdevices: Synthesis, Properties, and Structural Studies. Cryst. Growth Des. 2015,15, 5138–5148. [CrossRef] 10. Basavalingappa, V.; Bera, S.; Xue, B.; O’Donnell, J.; Guerin, S.; Cazade, P.A.; Yuan, H.; ul Haq, E.; Silien, C.; Tao, K.; et al. Diphenylalanine-Derivative Peptide Assemblies with Increased Aromaticity Exhibit Metal-like Rigidity and High Piezoelectricity. ACS Nano 2020,14, 7025–7037. [CrossRef] 11. Tao, K.; Xue, B.; Li, Q.; Hu, W.; Shimon, L.J.; Makam, P.; Si, M.; Yan, X.; Zhang, M.; Cao, Y.; et al. Stable and Optoelectronic Dipeptide Assemblies for Power Harvesting. Mater. Today 2019,30, 10–16. [CrossRef] [PubMed] 12. Zhao, L.; Yan, X. Supramolecular Self-Assembly: A Facile Way to Fabricate Protein and Peptide Nanomaterials. In Artificial Protein and Peptide Nanofibers; Elsevier: Amsterdam, The Netherlands, 2020; pp. 3–21. [CrossRef] 13. Tao, K.; Hu, W.; Xue, B.; Chovan, D.; Brown, N.; Shimon, L.J.W.; Maraba, O.; Cao, Y.; Tofail, S.A.M.; Thompson, D.; et al. Bioinspired Stable and Photoluminescent Assemblies for Power Generation. Adv. Mater. 2019 ,31, 1807481. [CrossRef] [PubMed] 14. Tao, K.; Makam, P.; Aizen, R.; Gazit, E. Self-Assembling Peptide Semiconductors. Science 2017 ,358, eaam9756. [CrossRef] [PubMed] 15. Azuri, I.; Adler-Abramovich, L.; Gazit, E.; Hod, O.; Kronik, L. Why Are Diphenylalanine-Based Peptide Nanostructures so Rigid? Insights from First Principles Calculations. J. Am. Chem. Soc. 2014,136, 963–969. [CrossRef] 16. Santos, D.; Baptista, R.M.F.; Handa, A.; Almeida, B.; Rodrigues, P.V.; Torres, A.R.; Machado, A.; Belsley, M.; de Matos Gomes, E. Bioinspired Cyclic Dipeptide Functionalized Nanofibers for Thermal Sensing and Energy Harvesting. Materials 2023 ,16, 2477. [CrossRef] 17. Haider, A.; Haider, S.; Kang, I.K. A Comprehensive Review Summarizing the Effect of Electrospinning Parameters and Potential Applications of Nanofibers in Biomedical and Biotechnology. Arab. J. Chem. 2018,11, 1165–1188. [CrossRef] 18. Pillay, V.; Dott, C.; Choonara, Y.E.; Tyagi, C.; Tomar, L.; Kumar, P.; du Toit, L.C.; Ndesendo, V.M.K. A Review of the Effect of Processing Variables on the Fabrication of Electrospun Nanofibers for Drug Delivery Applications. J. Nanomater. 2013 ,2013, 1–22. [CrossRef] 19. Stoller, P.; Reiser, K.M.; Celliers, P.M.; Rubenchik, A.M. Polarization-Modulated Second Harmonic Generation in Collagen. Biophys. J. 2002,82, 3330–3342. [CrossRef] 20. Handelman, A.; Shalev, G.; Rosenman, G. Symmetry of Bioinspired Short Peptide Nanostructures and Their Basic Physical Properties. Israel J. Chem. 2015,55, 637–644. [CrossRef] 21. Khanra, S.; Ghosh, K.; Ferreira, F.F.; Alves, W.A.; Punzo, F.; Yu, P.; Guha, S. Probing Nonlinear Optical Coefficients in SelfAssembled Peptide Nanotubes. Phys. Chem. Chem. Phys. 2017,19, 3084–3093. [CrossRef] 22. Briscoe, J.; Dunn, S. Piezoelectric Nanogenerators – a Review of Nanostructured Piezoelectric Energy Harvesters. Nano Energy 2015,14, 15–29. [CrossRef] 23. Viezbicke, B.D.; Patel, S.; Davis, B.E.; Birnie, D.P. Evaluation of the Tauc Method for Optical Absorption Edge Determination: ZnO Thin Films as a Model System: Tauc Method for Optical Absorption Edge Determination. Phys. Status Solidi (B) 2015 , 252, 1700–1710. [CrossRef] 24. Kortüm, G.; Braun, W.; Herzog, G. Principles and Techniques of Diffuse-Reflectance Spectroscopy. Angew. Chem. Int. Ed. Engl. 1963,2, 333–341. [CrossRef] 25. Zanatta, A.R. Revisiting the Optical Bandgap of Semiconductors and the Proposal of a Unified Methodology to Its Determination. Sci. Rep. 2019,9, 11225. [CrossRef] [PubMed] 26. Baptista, R.M.F.; Gomes, C.S.B.; Silva, B.; Oliveira, J.; Almeida, B.; Castro, C.; Rodrigues, P.V.; Machado, A.; Freitas, R.B.; Rodrigues, M.J.L.F.; et al. A Polymorph of Dipeptide Halide Glycyl-L-Alanine Hydroiodide Monohydrate: Crystal Structure, Optical Second Harmonic Generation, Piezoelectricity and Pyroelectricity. Materials 2023,16, 3690. [CrossRef] 27. You, Y.; Xing, R.; Zou, Q.; Shi, F.; Yan, X. High-Tolerance Crystalline Hydrogels Formed from Self-Assembling Cyclic Dipeptide. Beilstein J. Nanotechnol. 2019,10, 1894–1901. [CrossRef] 28. Macha, P.; Perreault, L.; Hamedani, Y.; Mayes, M.L.; Vasudev, M.C. Molecular Mechanisms of Tryptophan–Tyrosine Nanostructures Formation and Their Influence on PC-12 Cells. ACS Appl. Bio Mater. 2018,1, 1266–1275. [CrossRef] 29. Ryan, D.M.; Nilsson, B.L. Self-Assembled Amino Acids and Dipeptides as Noncovalent Hydrogels for Tissue Engineering. Polymer Chem. 2012,3, 18–33. [CrossRef] Materials 2023,16, 4993 17 of 17 30. Salzmann, C.G.; Ward, M.A.H.; Jacobs, R.M.J.; Tobias, G.; Green, M.L.H. Interaction of Tyrosine-, Tryptophan-, and LysineContaining Polypeptides with Single-Wall Carbon Nanotubes and Its Relevance for the Rational Design of Dispersing Agents. J. Phys. Chem. C 2007,111, 18520–18524. [CrossRef] 31. Baptista, R.M.F.; de Matos Gomes, E.; Raposo, M.M.M.; Costa, S.P.G.; Lopes, P.E.; Almeida, B.; Belsley, M.S. Self-Assembly of Dipeptide Boc-diphenylalanine Nanotubes inside Electrospun Polymeric Fibers with Strong Piezoelectric Response. Nanosc. Adv. 2019,1, 4339–4346. [CrossRef] 32. Costa, J.C.; Taveira, R.J.; Lima, C.F.; Mendes, A.; Santos, L.M. Optical Band Gaps of Organic Semiconductor Materials. Opt. Mater. 2016,58, 51–60. [CrossRef] 33. Baptista, R.M.F.; Moreira, G.; Silva, B.; Oliveira, J.; Almeida, B.; Castro, C.; Rodrigues, P.V.; Machado, A.; Belsley, M.; de Matos Gomes, E. Lead-Free MDABCO-NH4I3 Perovskite Crystals Embedded in Electrospun Nanofibers. Materials 2022 ,15, 8397. [CrossRef] [PubMed] 34. Maciel, M.; Ribeiro, S.; Ribeiro, C.; Francesko, A.; Maceiras, A.; Vilas, J.; Lanceros-Méndez, S. Relation between Fiber Orientation and Mechanical Properties of Nano-Engineered Poly(Vinylidene Fluoride) Electrospun Composite Fiber Mats. Comp. Part B Eng. 2018,139, 146–154. [CrossRef] 35. Jang, D.; Beckett, L.E.; Keum, J.; Korley, L.T. Leveraging Peptide–Cellulose Interactions to Tailor the Hierarchy and Mechanics of Peptide–Polymer Hybrids. J. Mater. Chem. B 2023,11, 5594–5606. [CrossRef] 36. Rubin, D.J.; Nia, H.T.; Desire, T.; Nguyen, P.Q.; Gevelber, M.; Ortiz, C.; Joshi, N.S. Mechanical Reinforcement of Polymeric Fibers through Peptide Nanotube Incorporation. Biomacromolecules 2013,14, 3370–3375. [CrossRef] 37. Dias, J.R.; Sousa, A.; Augusto, A.; Bártolo, P.J.; Granja, P.L. Electrospun Polycaprolactone (PCL) Degradation: An In Vitro and In Vivo Study. Polymers 2022,14, 3397. [CrossRef] [PubMed] 38. Gautam, S.; Chou, C.F.; Dinda, A.K.; Potdar, P.D.; Mishra, N.C. Fabrication and Characterization of PCL/Gelatin/Chitosan Ternary Nanofibrous Composite Scaffold for Tissue Engineering Applications. J. Mater. Sci. 2014,49, 1076–1089. [CrossRef] 39. Haifeng Wang.; Weiner, A. Efficiency of Short-Pulse Type-i Second-Harmonic Generation with Simultaneous Spatial Walk-off, Temporal Walk-off, and Pump Depletion. IEEE J. Quantum Electr. 2003,39, 1600–1618. [CrossRef] 40. Smith, A.V. Crystal Nonlinear Optics: With SNLO Examples, 2nd ed.; AS-Photonics: Albuquerque, NM, USA, 2018. 41. Baptista, R.M.F.; Lopes, P.E.; Rodrigues, A.R.O.; Cerca, N.; Belsley, M.S.; de Matos Gomes, E. Self-Assembly of Boc-p-NitroL -Phenylalanylp-Nitro-L-Phenylalanine and Boc-L-PhenylalanylL-Tyrosine in Solution and into Piezoelectric Electrospun Fibers. Mater. Adv. 2022,3, 2934–2944. [CrossRef] 42. Santos, D.F.M. Nanofibras Funcionalizadas com Dipéptidos Cíclicos para Aplicações em Biossensores. Master’s Thesis, University of Minho, Braga, Portugal, 2022. Available online: https://hdl.handle.net/1822/84545 (accessed on 13 February 2023). 43. Li, Q.; Jia, Y.; Dai, L.; Yang, Y.; Li, J. Controlled Rod Nanostructured Assembly of Diphenylalanine and Their Optical Waveguide Properties. ACS Nano 2015,9, 2689–2695. [CrossRef] 44. Pompa-Monroy, D.A.; Figueroa-Marchant, P.G.; Dastager, S.G.; Thorat, M.N.; Iglesias, A.L.; Miranda-Soto, V.; Pérez-González, G.L.; Villarreal-Gómez, L.J. Bacterial Biofilm Formation Using PCL/Curcumin Electrospun Fibers and Its Potential Use for Biotechnological Applications. Materials 2020,13, 5556. [CrossRef] [PubMed] Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.